Electrophotographic photoreceptor with bisazo compound

ABSTRACT

This invention provides an electrophotographic photoreceptor which is high in durability and high in sensitivity. This photoreceptor comprises an electroconductive support and, provided thereon, a photosensitive layer containing an azo pigment represented by the following formula [I] or [II]: ##STR1## wherein A represents a hydrogen atom, an alkyl group, a phenyl group or a heterocyclic ring group, m and n each represents 0 or 1, X represents a hydrogen atom, a lower alkyl group, a cyano group or a halogen atom and Cp represents a coupler residue, or ##STR2## wherein Z represents an alkyl group, a phenyl group or a heterocyclic ring group, X represents a hydrogen atom, a lower alkyl group, a cyano group or a halogen atom and Cp represents a coupler residue.

This application is a continuation of application Ser. No. 260,140,filed Oct. 20, 1988, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to an electrophotographic photoreceptor and,particularly, to a novel electrophotographic photoreceptor having aphotosensitive layer containing an azo pigment. More particularly, itrelates to a highly durable electrophotographic photoreceptor high insensitivity and suitable for repeated use.

Hitherto, there have been widely known those having a photosensitivelayer mainly composed of inorganic photoconductive materials such asselenium, zinc oxide and cadmium sulfide.

However, these photoreceptors are not necessarily satisfactory insensitivity, thermal stability, moisture resistance and durability.Especially, the toxicity of selenium and cadmium sulfide imposes somerestriction on their manufacture and handling.

On the other hand, recently, electrophotographic photoreceptors having aphotosensitive layer mainly composed of an organic photoconductivecompound have attracted much attention because of the ease of theirmanufacture and thermal stability superior to the seleniumphotoreceptors.

A well known organic photoconductive compound is poly-N-vinylcarbazole.However, an electrophotographic photoreceptor having a photosensitivelayer mainly composed of a charge transfer complex formed from thepoly-N-vinylcarbazole and a Lewis acid such as2,4,7-trinitro-9-fluorenone is not necessarily satisfactory insensitivity and durability.

Photoreceptors of functionally separated type such as a laminated typeand a dispersion type, in which the carrier generating function and thecarrier transfer function are respectively borne by different substanceshave advantages that the materials can be selected from a wide range andthus electrophotographic photoreceptors having any of characteristicssuch as charge characteristic, sensitivity and durability can berelatively easily produced.

Hitherto, various carrier generating materials and carrier transfermaterials have been proposed.

For example, electrophotographic receptors have been put to practicaluse which has a photosensitive layer comprising a combination of acarrier generating layer comprising amorphous selenium and a carriertransfer layer mainly composed of poly-N-vinylcarbazole. However, thecarrier generating layer comprising amorphous selenium is inferior indurability

Furthermore, use of organic dyes and pigments as a carrier generatingmaterial has been proposed and, for example, electrophotographicphotoreceptors containing monoazo pigment or bisazo pigment in thephotosensitive layer are disclosed in Japanese Patent Kokoku No.48-30513, Japanese Patent Kokai Nos. 52-4241 and 54-46558 and JapanesePatent Kokoku No. 56-11945. However, these azo pigments are notcompletely satisfactory in sensitivity, residual potential and stabilityin repeated use and besides, scope of selection of carrier transfermaterials is limited. Thus, the fact is that there are noelectrophotographic photoreceptors which fully meet a wide variety ofrequirements of the electrophotographic process.

SUMMARY OF THE INVENTION

An object of this invention is to provide an electrophotographicphotoreceptor containing an azo pigment which is stable against heat andlight and is excellent in carrier generating ability.

Another object of this invention is to provide an electrophotographicphotoreceptor high in sensitivity, small in residual potential andexcellent in durability, these properties being unaffected by repeateduse.

Still another object of this invention is to provide anelectrophotographic photoreceptor which contains an azo pigment capableof effectively functioning as carrier generating material even incombination with a wide variety of carrier transfer materials.

DESCRIPTION OF THE INVENTION

As a result of the inventors' intensive research, it has been found thatthe azo pigments represented by the following formula [I] or [II] canserve as effective component of photoreceptors. This invention is basedon this finding. ##STR3## wherein A represents a hydrogen atom, a alkylgroup, a phenyl group or a hetrocyclic group, m and n each represent 0or 1, X represents a hydrogen atom, a lower alkyl group, a cyano groupor a halogen atom and Cp represents a coupler residue. ##STR4## whereinZ represents an alkyl group, a phenyl group or a heterocyclic group, Xrepresents a hydrogen atom, a lower alkyl group, a cyano group or ahalogen atom and Cp represents a coupler residue.

Cp represents a residue of a coupler which reacts with diazo group andespecially effective coupler residues are as shown by the followingformula (III). ##STR5## [wherein Y represents a group of atoms necessaryto form a polycyclic aromatic ring such as, for example, naphthalene oranthracene ring by condensation with a benzene ring or to form aheterocyclic ring such as, for example, carbazole ring, benzocarbazolering or dibenzofuran ring by condensation with benzene ring; R₁represents an alkyl group which may be substituted (e.g., methyl, ethyl,n-propyl, iso-propyl, n-butyl, sec-butyl, amyl, l-octyl, benzyl,p-chlorobenzyl, 3,4-dichlorobenzyl, p-methylbenzyl, 2-phenylethyl,α-naphthylmethyl and β-naphthylmethyl) or an aryl group which may besubstituted (e.g., phenyl, tolyl, xylyl, biphenyl, chlorophenyl,dichlorophenyl, bromophenyl, methoxyphenyl, ethoxyphenyl, butoxyphenyl,phenoxyphenyl, nitrophenyl, cyanophenyl, hydroxyphenyl, carboxyphenyl,N,N-dimethylaminophenyl, α,α,α-trifluoromethylphenyl, methylthiophenyl,α-naphthyl and β-naphthyl); R₂ represents the same group as for R₁ or aheterocyclic group (e.g., thiazolyl, 5-nitrothiazolyl, carbazolyl,indolyl, pyrrolyl, acridyl, benzo(b)thiophenyl, benzoinimidazolyl,oxazolyl, chloroxazolyl, triazolyl, piperidyl, pyridyl and quinolyl); R₃represents O, S or --NH--, R₄ and R₅ each represents a hydrogen atom, analkyl which may be substituted, a nitro group, a methoxy group, anethoxy group, an acetyl group, a cyano group or a halogen atom; and Zrepresents a chain hydrocarbon group necessary to form a 5- or6-membered ring].

That is, according to this invention, an electrophotographicphotoreceptor which is excellent in film properties andelectrophotographic characteristics such as charge retention,sensitivity and residual potential, is suceptible to littledeterioration due fatigue after repeated use, shows no change in saidcharacteristics against exposure to heat and light and thus can exhibitstable characteristics can be produced by using the azo pigmentrepresented by the above formula [I] or [II] as a photoconductivematerial in a photosensitive layer of the electrophotographicphotoreceptor and as a carrier generating material of the functionallyseparated type, in which generation and transfer of carrier areperformed by different materials by utilizing only the superior carriergenerating ability of the azo pigment.

Examples of the azo pigments represented by the above formulas anduseful in this invention include those which have the followingstructural formulas, but this invention is not limited thereto.

Examples of azo pigments of the formula [I]:

    __________________________________________________________________________     ##STR6##                                                                     Azo pigment                                                                          X   A          n Cp                                                    __________________________________________________________________________    I-1    H   H          0                                                                                ##STR7##                                             I-2    H   H          1                                                                                ##STR8##                                             I-3    H   CH.sub.3   0                                                                                ##STR9##                                             I-4    H   CH.sub.3   0                                                                                ##STR10##                                            I-5    H   C.sub.2 H.sub.5                                                                          0                                                                                ##STR11##                                            I-6    H   C.sub.2 H.sub.5                                                                          0                                                                                ##STR12##                                            I-7    H                                                                      nC.sub.3 H.sub.7                                                                     0                                                                                  ##STR13##                                                         I-8    H                                                                      nC.sub.4 H.sub.9                                                                     0                                                                                  ##STR14##                                                         I-9    H   CH.sub.2 Cl                                                                              0                                                                                ##STR15##                                            I-10   H   CHClH.sub.3                                                                              0                                                                                ##STR16##                                            1-11   H   CHClCH.sub.3                                                                             0                                                                                ##STR17##                                            I-12   H                                                                                  ##STR18## 0                                                                                ##STR19##                                            I-13   H                                                                                  ##STR20## 0                                                                                ##STR21##                                            I-14   H                                                                                  ##STR22## 1                                                                                ##STR23##                                            I-15   H                                                                                  ##STR24## 0                                                                                ##STR25##                                            I-16   H                                                                                  ##STR26## 1                                                                                ##STR27##                                            I-17   H                                                                                  ##STR28## 0                                                                                ##STR29##                                            I-18   H                                                                                  ##STR30## 1                                                                                ##STR31##                                            I-19   H                                                                                  ##STR32## 0                                                                                ##STR33##                                            I-20   H                                                                                  ##STR34## 0                                                                                ##STR35##                                            I-21   H                                                                                  ##STR36## 0                                                                                ##STR37##                                            I-22   H                                                                                  ##STR38## 0                                                                                ##STR39##                                            I-23   H                                                                                  ##STR40## 0                                                                                ##STR41##                                            I-24   CN                                                                                 ##STR42## 1                                                                                ##STR43##                                            I-25   CN  CH.sub.3   0                                                                                ##STR44##                                            I-26   CN  C.sub.2 H.sub.5                                                                          0                                                                                ##STR45##                                            I-27   CN                                                                                 ##STR46## 0                                                                                ##STR47##                                            I-28   CN                                                                                 ##STR48## 1                                                                                ##STR49##                                            I-29   CN                                                                                 ##STR50## 0                                                                                ##STR51##                                            I-30   CN                                                                                 ##STR52## 0                                                                                ##STR53##                                            I-31   CN                                                                                 ##STR54## 0                                                                                ##STR55##                                            I-32   CN                                                                                 ##STR56## 1                                                                                ##STR57##                                            I-33   CN                                                                                 ##STR58## 0                                                                                ##STR59##                                            I-34   CN                                                                                 ##STR60## 0                                                                                ##STR61##                                            I-35   CH.sub.3                                                                          C.sub.2 H.sub.5                                                                          0                                                                                ##STR62##                                            I-36   CH.sub.3                                                                           ##STR63##                                                                                  ##STR64##                                            I-37   CH.sub.3                                                                           ##STR65##                                                                                  ##STR66##                                            I-38   CH.sub.3                                                                           ##STR67##                                                                                  ##STR68##                                            I-39   Cl                                                                                 ##STR69##                                                                                  ##STR70##                                            I-40   Cl  H                                                                                           ##STR71##                                            I-41   Br  H          0                                                                                ##STR72##                                            I-42   Br                                                                                 ##STR73## 0                                                                                ##STR74##                                            __________________________________________________________________________

    __________________________________________________________________________     ##STR75##                                                                    Azo pigment                                                                           X    A                  Cp                                            __________________________________________________________________________    I-43    H    H                                                                                                 ##STR76##                                    I-44    H                                                                                   ##STR77##                                                                                        ##STR78##                                    I-45    H                                                                                   ##STR79##                                                                                        ##STR80##                                    I-46    H                                                                                   ##STR81##                                                                                        ##STR82##                                    I-47    H                                                                                   ##STR83##                                                                                        ##STR84##                                    I-48    CH.sub.3                                                                            ##STR85##                                                                                        ##STR86##                                    I-49    CN   H                                                                                                 ##STR87##                                    I-50    CN   H                                                                                                 ##STR88##                                    I-51    CN                                                                                  ##STR89##                                                                                        ##STR90##                                    I-52    CN                                                                                  ##STR91##                                                                                        ##STR92##                                    I-53    CN                                                                                  ##STR93##                                                                                        ##STR94##                                    I-54    CN                                                                                  ##STR95##                                                                                        ##STR96##                                    I-55    Cl   H                                                                                                 ##STR97##                                    I-56    Cl                                                                                  ##STR98##                                                                                        ##STR99##                                    I-57    Cl                                                                                  ##STR100##                                                                                       ##STR101##                                   I-58    Br   H                                                                                                 ##STR102##                                   I-59    Br                                                                                  ##STR103##                                                                                       ##STR104##                                   I-60    I    C.sub.2 H.sub.5                                                                                   ##STR105##                                   __________________________________________________________________________

    __________________________________________________________________________     ##STR106##                                                                   Azo pigment                                                                           X    A            Cp                                                  __________________________________________________________________________    I-61    H    H                                                                                           ##STR107##                                         I-62    H    C.sub.2 H.sub.5                                                                             ##STR108##                                         I-63    H                                                                                   ##STR109##                                                                                 ##STR110##                                         I-64    CN                                                                                  ##STR111##                                                                                 ##STR112##                                         I-65    CN                                                                                  ##STR113##                                                                                 ##STR114##                                         __________________________________________________________________________     ##STR115##                                                                   Azo pigment                                                                          A          n  Cp                                                       __________________________________________________________________________    I-66   H          0                                                                                 ##STR116##                                              I-67   H          1                                                                                 ##STR117##                                              I-68   CH.sub.3   0                                                                                 ##STR118##                                              I-69   CH.sub.3   0                                                                                 ##STR119##                                              I-70   C.sub.2 H.sub.5                                                                          0                                                                                 ##STR120##                                              I-71   C.sub.2 H.sub.5                                                                          0                                                                                 ##STR121##                                              I-72                                                                          nC.sub.3 H.sub.9                                                                     0                                                                                         ##STR122##                                                 I-73                                                                          nC.sub.4 H.sub.9                                                                     0                                                                                         ##STR123##                                                 I-74   CH.sub.2 Cl                                                                              0                                                                                 ##STR124##                                              I-75   CHClCH.sub.3                                                                             0                                                                                 ##STR125##                                              I-76   CHClCH.sub.3                                                                             0                                                                                 ##STR126##                                              I-77                                                                                  ##STR127##                                                                              0                                                                                 ##STR128##                                              I-78                                                                                  ##STR129##                                                                              0                                                                                 ##STR130##                                              I-79                                                                                  ##STR131##                                                                              1                                                                                 ##STR132##                                              I-80                                                                                  ##STR133##                                                                              0                                                                                 ##STR134##                                              I-81                                                                                  ##STR135##                                                                              1                                                                                 ##STR136##                                              I-82                                                                                  ##STR137##                                                                              0                                                                                 ##STR138##                                              I-83                                                                                  ##STR139##                                                                              1                                                                                 ##STR140##                                              I-84                                                                                  ##STR141##                                                                              0                                                                                 ##STR142##                                              I-85                                                                                  ##STR143##                                                                              0                                                                                 ##STR144##                                              I-86                                                                                  ##STR145##                                                                              0                                                                                 ##STR146##                                              I-87                                                                                  ##STR147##                                                                              0                                                                                 ##STR148##                                              I-88                                                                                  ##STR149##                                                                              0                                                                                 ##STR150##                                              I-89                                                                                  ##STR151##                                                                              1                                                                                 ##STR152##                                              __________________________________________________________________________     ##STR153##                                                                   Azo pigment                                                                            A            Cp                                                      __________________________________________________________________________    I-90     H                                                                                           ##STR154##                                             I-91                                                                                    ##STR155##                                                                                 ##STR156##                                             I-92                                                                                    ##STR157##                                                                                 ##STR158##                                             I-93                                                                                    ##STR159##                                                                                 ##STR160##                                             I-94                                                                                    ##STR161##                                                                                 ##STR162##                                             I-95                                                                                    ##STR163##                                                                                 ##STR164##                                             I-96     H                                                                                           ##STR165##                                             I-97                                                                                    ##STR166##                                                                                 ##STR167##                                             I-98                                                                                    ##STR168##                                                                                 ##STR169##                                             I-99                                                                                    ##STR170##                                                                                 ##STR171##                                              I-100                                                                                  ##STR172##                                                                                 ##STR173##                                              I-101   H                                                                                           ##STR174##                                              I-102                                                                                  ##STR175##                                                                                 ##STR176##                                              I-103   H                                                                                           ##STR177##                                              I-104                                                                                  ##STR178##                                                                                 ##STR179##                                             __________________________________________________________________________

Among the azo pigments represented by the above formula [I], thoserepresented by the following formula [I-A] have the maximum spectralsensitivity in the region of about 500 nm-about 600 nm and thesensitivity is sharply cut off on longer wavelength side. Therefore,they are excellent in reproducibility of red color of the original andbesides, have high sensitivity and low residual potential and excellentin preexposure characteristics and characteristics after repeated use asphotoreceptors used in electrophotographic copier with a halogen lamp asa light source. ##STR180## (wherein R₁ represents a hydrogen atom, alower alkyl group, a lower alkoxy group or a halogen atom; Cp represents##STR181## R₂ represents a hydrogen atom, a lower alkyl group, a loweralkoxy group or a halogen atom; n represents 0 or 1, l and p eachrepresents 1 or 2 and when l and p are 2, and two R₁ and the two R₂ maybe identical or different, respectively.

Examples of the azo pigments represented by the formula [I-A] are asfollows:

    ______________________________________                                        Examples of the pigments of the formula [I-A]                                 Azo pigment  R.sub.1     R.sub.2     n                                        ______________________________________                                        I-105        H           (2)--Cl     0                                        I-106        H           (2)--Br     0                                        I-107        (4)--CH.sub.3                                                                             (2)--Br     0                                        I-108        (4)--C.sub.2 H.sub.5                                                                      (2)--Br     0                                        I-109        H           (2)--CH.sub.3                                                                             0                                        I-110        (4)--CH.sub.3                                                                             (4)--Cl     1                                        I-111        (2)--CH.sub.3                                                                             (2)--Br     0                                                     (4)--CH.sub.3                                                    I-112        (4)--C.sub.2 H.sub.5                                                                      H           1                                        I-113        (4)--Cl     (3)--Cl     0                                                                 (4)--Cl                                              I-114        (4)--CH.sub.3                                                                             (2)--CH.sub.3                                                                             0                                        I-115        (3)--OCH.sub.3                                                                            H           1                                        I-116        H           H           1                                        I-117        (4)--CH.sub.3                                                                             (2)--CF.sub.3                                                                             0                                        I-118        (2)--Br     H           0                                        I-119        (4)--Br     (2)--C.sub.2 H.sub.5                                                                      0                                        I-120        (4)--C.sub.2 H.sub.5                                                                      (2)--CH.sub.3                                                                             1                                        I-121        (4)--CH.sub.3                                                                             (2)--Br     0                                                                 (4)--Br                                              I-122        H           (2)--Cl     0                                                                 (4)--CH.sub.3                                        I-123                    (2)--CH.sub.3                                                                             0                                                                 (4)--CH.sub.3                                        I-124        (2)--CH.sub.3                                                                             (2)--Cl     0                                                     (4)--Cl                                                          ______________________________________                                    

Examples of azo pigments of the formula [II]:

    __________________________________________________________________________    Azo pigment                                                                           Z              X     Cp                                               __________________________________________________________________________     ##STR182##                                                                   II-1                                                                                   ##STR183##    H                                                                                    ##STR184##                                      II-2                                                                                   ##STR185##    H                                                                                    ##STR186##                                      II-3                                                                                   ##STR187##    H                                                                                    ##STR188##                                      II-4                                                                                   ##STR189##    H                                                                                    ##STR190##                                      II-5                                                                                   ##STR191##    Cl                                                                                   ##STR192##                                      II-6                                                                                   ##STR193##    Cl                                                                                   ##STR194##                                      II-7                                                                                   ##STR195##    CH.sub.3                                                                             ##STR196##                                      II-8                                                                                   ##STR197##    CN                                                                                   ##STR198##                                      II-9                                                                                   ##STR199##    CN                                                                                   ##STR200##                                      II-10                                                                                  ##STR201##    CN                                                                                   ##STR202##                                      II-11                                                                                  ##STR203##    CN                                                                                   ##STR204##                                      II-12                                                                                  ##STR205##    CN                                                                                   ##STR206##                                      II-13                                                                                  ##STR207##    H                                                                                    ##STR208##                                      II-14                                                                                  ##STR209##    H                                                                                    ##STR210##                                      II-15                                                                                  ##STR211##    H                                                                                    ##STR212##                                      II-16                                                                                  ##STR213##    H                                                                                    ##STR214##                                      II-17                                                                                  ##STR215##    Br                                                                                   ##STR216##                                      II-18                                                                                  ##STR217##    CN                                                                                   ##STR218##                                      II-19                                                                                  ##STR219##    CN                                                                                   ##STR220##                                      II-20                                                                                  ##STR221##    CH.sub.3                                                                             ##STR222##                                      II-21                                                                                  ##STR223##    H                                                                                    ##STR224##                                      II-22                                                                                  ##STR225##    H                                                                                    ##STR226##                                      II-23                                                                                  ##STR227##    H                                                                                    ##STR228##                                      II-24                                                                                  ##STR229##    CN                                                                                   ##STR230##                                      II-25                                                                                  ##STR231##    Cl                                                                                   ##STR232##                                      II-26                                                                                  ##STR233##    CN                                                                                   ##STR234##                                      II-27                                                                                  ##STR235##    CN                                                                                   ##STR236##                                      II-28                                                                                  ##STR237##    H                                                                                    ##STR238##                                      II-29                                                                                  ##STR239##    H                                                                                    ##STR240##                                      II-30   CH.sub.3       CN                                                                                   ##STR241##                                      II-31   CH.sub.3       H                                                                                    ##STR242##                                      II-32   C.sub.2 H.sub.5                                                                              H                                                                                    ##STR243##                                      II-33   C.sub.2 H.sub.5                                                                              H                                                                                    ##STR244##                                      II-34   C.sub.2 H.sub.4 OH                                                                           CN                                                                                   ##STR245##                                      II-35                                                                         nC.sub.3 H.sub.7                                                                      Cl                                                                                            ##STR246##                                            II-36   C.sub.2 H.sub.4 CN                                                                           H                                                                                    ##STR247##                                      II-37   CH.sub.2CHCH.sub.2                                                                           C.sub.2 H.sub.5                                                                      ##STR248##                                      II-38   CH.sub.2CHCH.sub.2                                                                           CN                                                                                   ##STR249##                                      II-39                                                                                  ##STR250##    H                                                                                    ##STR251##                                      II-40                                                                                  ##STR252##    CN                                                                                   ##STR253##                                      II-41                                                                                  ##STR254##    CN                                                                                   ##STR255##                                      II-42                                                                                  ##STR256##    H                                                                                    ##STR257##                                      II-43                                                                                  ##STR258##    H                                                                                    ##STR259##                                      II-44                                                                                  ##STR260##    CN                                                                                   ##STR261##                                      II-45                                                                                  ##STR262##    CH.sub.3                                                                             ##STR263##                                      II-46                                                                                  ##STR264##    CN                                                                                   ##STR265##                                      II-47                                                                                  ##STR266##    H                                                                                    ##STR267##                                      II-48                                                                                  ##STR268##    Cl                                                                                   ##STR269##                                       ##STR270##                                                                   II-49                                                                                  ##STR271##    H                                                                                    ##STR272##                                      II-50                                                                                  ##STR273##    H                                                                                    ##STR274##                                      II-51                                                                                  ##STR275##    H                                                                                    ##STR276##                                      II-52                                                                                  ##STR277##    CN                                                                                   ##STR278##                                      II-53   CH.sub.3       H                                                                                    ##STR279##                                      II-54   CH.sub.3       CN                                                                                   ##STR280##                                      II-55                                                                                  ##STR281##    CN                                                                                   ##STR282##                                      II-56   CH.sub.2CHCH.sub.2                                                                           CN                                                                                   ##STR283##                                      II-57   CH.sub. 2CHCH.sub.2                                                                          CN                                                                                   ##STR284##                                      II-58                                                                                  ##STR285##    H                                                                                    ##STR286##                                      II-59                                                                                  ##STR287##    CH.sub.3                                                                             ##STR288##                                      II-60                                                                                  ##STR289##    H                                                                                    ##STR290##                                      II-61                                                                                  ##STR291##    CN                                                                                   ##STR292##                                      II-62                                                                                  ##STR293##    CN                                                                                   ##STR294##                                      II-63                                                                                  ##STR295##    CN                                                                                   ##STR296##                                      __________________________________________________________________________

The azo pigments represented by the formula [I] or [II] can be easilysynthesized by customarily azotizing a divalent amino compoundrepresented by the following formula: ##STR297## and then coupling witha corresponding coupler in the presence of an alkali or, alternatively,isolating the diazonium salt of said divalent amino compound in the formof borofluoride or zinc chloride double salt and coupling with a couplerin the presence of an organic or inorganic alkali in a suitable solventsuch as, for example, N,N-dimethylformamide, dimethyl sulfoxide, ethanolor dioxane.

Synthesis of typical examples of the azo pigments used in this inventionis described below.

SYNTHESIS EXAMPLE 1 Azo pigment No. I-13

Acetophenone and p-nitrohydrazine in equimolar amount were allowed toreact in ethanol to obtain acetophenone-p-nitrophenylhydrazone. Theresulting hydrazone was converted to a pyrazole compound represented bythe following structural formula using phosphorus oxychloride anddimethylformamide. ##STR298##

The resulting aldehyde derivative of pyrazole and p-nitrobenzyl cyanidewere dissolved in dioxane and the solution was reacted with piperidineto obtain 1-(p-nitrophenyl)-3-phenyl-4-(β-cyano-p-nitrostyryl)pyrazole.

Recrystallization was effected with pyridine.

The resulting dinitro derivative was reduced with iron powder andglacial acetic acid to easily obtain a diamino compound represented bythe following structural formula: ##STR299##

Upon examination of the IR absorption (KBr method), it was found thatabsorption at 1340 cm⁻¹ due to a nitro group disappeared and, instead,an absorption due to amino group was observed at 3320 cm⁻¹. Further,there was observed absorption at 2200 cm⁻¹ due to cyano group.

0.75 g of the thus obtained diamino compound was dissolved in 20 ml of2N-hydrochloric acid and insoluble matters were removed. Then, to thesolution was added dropwise a solution prepared by dissolving 0.5 g ofsodium nitrite in a minimum amount of water under ice cooling to allowthe reaction to proceed for about 1 hour. Then, active carbon was addedthereto, followed by filtration to obtain a diazonium solution.

1.2 g of 2-hydroxy-N-(4-cyanophenyl)-3-naphthoic acid amide and 1.0 g oftriethylamine were dissolved in 20 ml of dimethyl sulfoxide and thesolution was cooled to 0°-5° C. to obtain a coupling component.

Then, the above diazonium salt solution was added dropwise to the abovecoupler solution and the resulting blackish purple pasty solution waskept at 0°-10° C. and stirred for 3 hours. The resulting precipitate wascollected by filtration, fully washed with dimethylformamide, then withhot water and finally with acetone and dried at 80° C. for about 5 hoursto obtain 1.05 g of black powder having somewhat metallic luster andhaving a decomposition point of about 345° C.

SYNTHESIS EXAMPLE 2 Azo pigment No. I-105

10.2 g of acetophenone -p-nitrophenylhydrazone (melting point:186.5°-188.0° C.) obtained by equimolar reaction ofp-nitrophenylhydrazine and acetophenone was subjected to Vilsmeirreaction with phosphorus oxychloride and dimethylformamide to obtain11.8 g of 1-(p-nitrophenyl)-3-phenylpyrazole-4-carboxyaldehyde (meltingpoint: 208.5°-211.0° C.) having the following structural formula.##STR300##

6.0 g of the thus obtained pyrazole compound and 6.0 g ofdiethyl-p-nitrobenzyl phosphonate were reacted in the presence ofpotassium tert-butoxide to obtain 8.2 g of yellow1-(p-nitrophenyl)-3-phenyl-4-(p-nitrostylyl)pyrazole (melting point:228°-233° C.).

The resulting dinitro derivative of pyrazole was reduced with ironpowder and glacial acetic acid to obtain a diamino compound of pyrazoleof light brown and having the following structural formula (meltingpoint: 153.5°-156.0° C.). ##STR301##

2.12 g of the above diamino compound was dispersed in 40 ml of 1 Nhydrochloric acid and thereto was added an aqueous solution containing0.9 g of sodium nitrite in 3.0 ml of water under ice cooling to producean aqueous diazonium salt solution.

The resulting aqueous diazonium salt solution was added dropwise to asolution prepared by dissolving 3.6 g of 2-hydroxy-3-naphthoic acido-chloroanilide and 8.0 g of triethylamine in dimethylformamide at roomtemperature. After stirring for about 2 hours, the precipitated reddishpurple powder was collected by filtration and well washed with water anddimethylformamide and finally with acetone to obtain 5.4 g of raddishpurple crystal having somewhat metallic luster. Melting point: 250° C.or higher.

SYNTHESIS EXAMPLE 3 Azo pigment No. II-9 Synthesis of tetrazonium salt

A 97% aqueous sodium nitrite solution was added dropwise at 0°-5° C. toa mixture comprising 3.8 g of1-phenyl-3-(4'-aminophenyl)-4-(4"-amino-β-cyanostyryl)-pyrazole havingthe following formula and a melting point of 247°-249° C., 40 ml of 6Nhydrochloric acid and 60 ml of water, followed by stirring for 1 hour atthis temperature. A small amount of insoluble matter was removed byfiltration and to the residue was added 42% borofluoric acid and theprecipitated crystal was collected by filtration, washed with water anddried to yield a tetrazonium salt. Yield: 4.1 g. ##STR302##

Synthesis of azo pigment No. II-9

1.4 g of the above tetrazonium salt and 1.9 g of a coupler having2-hydroxy-benzo[a]carbazole skeleton were dissolved in 100 ml ofN,N-dimethylformamide and to the solution was added dropwise at 5°-10°C. C over a period of 10 minutes a solution prepared by dissolving 1.5 gof triethanolamine in 10 ml of dimethylformamide, followed by stirringat room temperature for 3 hours. Then, the resulting precipitate wascollected by filtration, thoroughly washed with water and then withacetone to yield 3.1 g of a blackish blue powder. Melting point: 340° C.or higher.

Other azo pigments of this invention can also be obtained in a mannersimilar to the above synthetic exmaples.

The electrophotographic photoreceptor of this invention has aphotosensitive layer containing at least one azo pigments represented bythe formula [I] or [II]. There are known various types of photosensitivelayer. The photosensitive layer of the electrophotographic photoreceptorof this invention may be any of the known types, but is normally of thefollowing types:

(1) A photosensitive layer comprising an azo pigment.

(2) A photosensitive layer comprising a dispersion of an azo pigment ina binder.

(3) A photosensitive layer comprising a dispersion of an azo pigment ina known charge transfer material.

(4) A photosensitive layer of a laminate type comprising thephotosensitive layer (1), (2) or (3) as a charge generating layer and acharge transfer layer containing known charge transfer material.

The azo pigment represented by the above formulas generates in a highefficiency a charge carrier upon absorption of light. The generatedcarrier can be transferred through the medium of the azo pigment, butmore desirably through the medium of a known charge transfer material.From such a viewpoint, the photosensitive layers of the types (3) and(4) are especially preferred.

The charge transfer materials are generally classified into two groups,the first group which transfer the charge by electron propagation andthe second group which transfer the charge by hole propagation.Materials of both groups can be used in the photosensitive layer of thephotoreceptor of this invention. Mixtures of those which have the samefunctions or of those which have different functions may also be used.

The materials of the first group are electron attractive compoundshaving electron attractive groups such as nitro group, cyano group,ester group and the like. As examples thereof, mention may be made ofnitrated fluorenones such as 2,4,7-trinitrofluorenone and2,4,5,7-tetranitrofluorenone; tetracyanoquinodimethane,tetracyanoethylene, 2,4,5,7-tetranitroxanthone,2,4,8-trinitrothioxanthone and polymers of these compounds.

The materials of the second group are electron donative, organicphotoconductive compounds. Examples thereof are shown below: ##STR303##Further, there may also be used polymeric compounds such aspoly-N-vinylcarbazole, halogenated poly-N-vinylcarbazole,polyvinylpyrene, polyvinylanthracene, polyvinylacridine,polyglycidylcarbazole, polyvinylacenaphthylene and ethylcarbazoleformaldehyde resin.

The carrier transfer materials are not limited to those mentioned hereand may be used alone or in combination of two or more.

The electrophotographic photoreceptor of this invention can be preparedby conventional methods.

For example, the electrophotographic photoreceptor having thephotosensitive layer of type (1) can be prepared by dissolving ordispersing the azo pigment represented by the formula [I] or [II] in asuitable medium and coating the resulting coating composition on anelectroconductive support and drying the coat to form a photosensitivelayer of normally 0.1-several ten μm thick.

As the medium for preparation of the coating composition, mention may bemade of, for example, basic solvents which dissolves azo dyes such asn-butylamine and ethylenediamine and those which disperse azo pigments,for example, ethers such as tetrahydrofuran and 1,4-dioxane; ketonessuch as methyl ethyl ketone and cyclohexanone; aromatic hydrocarbonssuch as toluene and xylene; non-protonic polar solvents such asN,N-dimethylformamide, acetonitrile, N-methylpyrrolidone and dimethylsulfoxide; alcohols such as methanol, ethanol and isopropanol; esterssuch as ethyl acetate, methyl acetate and methyl cellosolve acetate; andchlorinated hydrocarbons such as dichloroethane and chloroform.

In case of using media which disperse azo pigments, azo pigments must bepulverized to a particle size of 5 μm or less, preferably 3 μm or lessand most suitably 1 μm or less.

As the electroconductive supports on which a photosensitive layer isformed, there may be any of those which are normally used forelectrophotographic photoreceptors.

Specific examples thereof are metallic drums or sheets of, for example,aluminum and copper and laminates of these metal foils and sheetsvapor-deposited with such metals.

Further examples of the supports are plastic films, plastic drums andpapers made electroconductive by coating with electroconductivematerials such as metallic powders, carbon black, copper iodide andpolymeric electrolytes together with suitable binders. Furthermore,there may also be used plastic sheets or drums made conductive bycontaining conductive materials such as metallic powder, carbon blackand carbon fibers.

The photoreceptor having a photosensitive layer of type (2) can beprepared by dissolving a binder in the coating composition used forformation of the photosensitive layer of type (1).

In this case, the medium of the coating composition is preferably onewhich dissolves binder.

As binders, mention may be made of, for example, polymers and copolymersof vinyl compounds such as styrene, vinyl acetate, acrylic esters andmethacrylic esters and polymers such as phenoxy resins, polysulfones,arylate resins, polycarbonates, polyesters, cellulose esters, celluloseethers, butyral resins, epoxy resins and acrylpolyol resins.

Amount of binder is usually 0.1-5 parts by weight for 1 part of azopigment.

In making such a type of photosensitive layer, it is desirable to allowazo pigments to be present in the form of fine particles such as, forexample, of 3 μm or less, especially 1 μm or less in particle size inthe binder.

Likewise, the photoreceptor having a photosensitive layer of type (3)can be prepared by dissolving a charge transfer medium in the coatingcomposition used for preparation of the photosensitive layer of type(1). Any of the abovementioned charge transfer media can be used.

The charge transfer medium is used preferably together with a binder,except for polyvinylcarbazole and polyglycidylcarbazole which serve alsoas binders. Any of the binders mentioned above can be used.

The binder is used normally in an amount of 0.5-100 parts by weight for1 part by weight of azo pigment. The charge transfer medium is usednormally in an amount of 0.2-3.0, preferably 0.3-1.2 parts by weight for1 part by weight of azo pigment. The charge transfer medium which servesalso as a binder is normally used in an amount of 1-10 parts by weightfor 1 part by weight of azo pigment.

Like the photosensitive layer of type (3), in the photosensitive layerof this type, azo pigment is preferably present in the form of fineparticles in the charge transfer medium and the binder.

The photoreceptors having a photosensitive layer of type (4) can beprepared by coating a coating composition prepared by dissolving acharge transfer medium in a suitable medium on the photosensitive layerof type (1), (2) or (3) and drying the coat, resulting in a chargetransfer layer on the photosensitive layer.

In this case, the photosensitive layers of types (1), (2) and (3) serveas charge generating layer. The charge transfer layer is not necessarilyprovided on the charge generating layer, but can be provided between thecharge generating layer and the conductive support. However, the formerstructure is preferred from the point of durability.

The charge transfer layer is formed in the similar manner to that forformation of the photosensitive layer of type (3). That is, there may beused the coating composition used for formation of the photosensitivelayer of type (3) from which azo pigment is omitted.

Thickness of the charge transfer layer is ordinarily 5-50 μm.

Of course, the photosensitive layer of the electrophotographicphotoreceptor of this invention may contain known sensitizers.

Suitable sensitizers include Lewis acids and dyes capable of forming acharge transfer complex with organic photoconductive materials.

As Lewis acids, mention may be made of, for example, quinones such aschloranil, 2,3-dichloro-l,4-naphthoquinone, 2-methylanthraquinone,1-nitroanthraquinone, 1-chloro-5-nitroanthraquinone,2-chloroanthraquinone and phenanthrenequinone; aldehydes such as4-nitrobenzaldehyde; ketones such as 9-benzoylanthracene, indanedione,3,5-dinitrobenzophenone and 3,3',5,5-tetranitrobenzophenone; acidanhydrides such as phthalic anhydride and 4-chloronaphthalic anhydride;cyano compounds such as tetracyanoethylene, terephthalmalonodinitrileand 4-nitrobenzalmalononitrile; and other electron attractive compoundssuch as 3-benzalphthalide, 3-(α-cyano-p-nitrobenzal)phthalide and3-(α-cyano-p-chlorobenzal)phthalide.

As examples of suitable dyes, mention may be made of triphenylmethanedyes such as Methyl Violet, Brilliant Green and Crystal Violet; thiazinedyes such as Methylene Blue; quinone dyes such as Quinizarin; cyaninedyes, pyrylium salts, thiapyrylium salts and benzopyrylium salts.

The photosensitive layer can also contain inorganic photoconductive fineparticles such as selenium an selenium-arsenic alloys and organicphotoconductive pigments such as copper-phthalocyanine pigments andperylene pigments.

The photosensitive layer of the photoreceptor of this invention canfurther contain known plasticizers to improve film-forming property,flexibility and mechanical strength. Suitable plasticizers includephthalate esters, phosphate esters, epoxy compounds, chlorinatedparaffins, chlorinated fatty acid esters, and aromatic compounds such asalkylated naphthalenes.

The photoreceptor of this invention may, of course, contain, ifnecessary, an adhesive layer, an intermediate layer, an insulatinglayer, and a protective layer.

The photoreceptor containing azo pigment according to this invention ishigh in sensitivity, superior in color sensitivity and upon repeated useshows little change in sensitivity and charge accepting property, littlefatigue and excellent durability.

Furthermore, the photoreceptor of this invention can be used not only inelectrophotographic copier but also widely in other electrophotographicfields such as printers using lasers, Braun tube (CRT) andlight-emitting diodes (LED) as light source.

The following nonlimiting examples further illustrate the invention.

EXAMPLE 1

On a conductive support of a polyester film clad with aluminum foil(ALPET 85 supplied by Daido Kako Co.; 10 μ in aluminum foil thickness)was formed an intermediate layer, 0.05 μ in thickness, of a vinylchloride-vinyl acetate-maleic anhydride copolymer (ESUREK MF-10 suppliedby Sekisui Chemical Co.). A carrier generating layer was formed bycoating on said intermediate layer an azo pigment dispersion prepared byadding 2 g of the aforementioned azo pigment No. I-12 and 1 g of abutyral resin (ESUREK B supplied by Sekisui Chemical Co.) in 100 ml oftetrahydrofuran and dispersing in a paint conditioner for about 1 hour,at a dry thickness of 0.3 μ. A carrier transfer layer, 19 μ in drythickness, was formed thereon by coating on the carrier generating layera solution comprising 5 g ofN,N-dibenzylaminobenzaldehyde-1,1-diphenylhydrazone, a carrier transfermaterial, and 7 g of a polyarylate resin dissolved in 50 ml of1,2-dichloroethane and drying the coating to obtain theelectrophotographic photoreceptor of this invention. This photoreceptorwas left to stand in the dark place at 30° C. for 1 week and thenmounted on an electrostatic paper testing apparatus (SP-428 supplied byKawaguchi Denki Seisakusho Co.) and tested for the characteristics inthe following manner.

That is, the photosensitive layer was electrostatically charged bysubjecting it for 5 seconds to the corona discharge produced byapplication of a potential of -6 KV by a charger and the surfacepotential V_(o) (-V) was measured. Then, the charged surface was exposedto a halogen lamp with the illuminance on the surface of thephotosensitive layer being 30 lux, and the exposure E_(1/2) (lux·second)necessary to decay the surface potential of the photosensitive layer to1/2 was measured.

Further, surface potential after having been exposed with an exposure of50 lux·second, namely, residual potential E₅₀ (-V) was determined.Similar test cycle was repeated 500 times. In each cycle, completeremoval of the residual potential was effected by exposing to a tungstenlamp for 0.3 second at 300 lux. The results are shown in Table 1.

                  TABLE 1                                                         ______________________________________                                                     First cycle                                                                           500th cycle                                              ______________________________________                                        V.sub.o (-V)   1040      1000                                                 E.sub.1/2  (lux · sec)                                                              2.0       1.9                                                  E.sub.50 (-V)  0-5       0                                                    ______________________________________                                    

EXAMPLES 2-6

Five photoreceptors of this inventions were prepared in the same manneras in Example 1 except that aforementioned azo pigment Nos. I-1, I-28,I-35, I-54 and I-63 were used as carrier generating materials. Eachphotoreceptor was tested for the characteristics as in Example 1. Theresults are shown in Table 2.

                                      TABLE 2                                     __________________________________________________________________________                  First cycle   500th cycle                                                     V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                                                          V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                Example                                                                            Azo pigments                                                                           (-V)                                                                              (lux · sec)                                                                (-V)                                                                              (-V)                                                                              (lux · sec)                                                                (-V)                                    __________________________________________________________________________    2    Pigment No. I-1                                                                         980                                                                              2.8   about                                                                              980                                                                              2.7   about                                                           15            20                                      3    Pigment No. I-28                                                                       1080                                                                              2.1   about                                                                             1040                                                                              2.1   0                                                               10                                                    4    Pigment No. I-35                                                                        880                                                                              1.9   about                                                                              870                                                                              1.9   0                                                               0-5                                                   5    Pigment No. I-54                                                                       1010                                                                              2.7   about                                                                              990                                                                              2.7   about                                                           15            10                                      6    Pigment No. I-63                                                                        980                                                                              2.2   about                                                                              940                                                                              2.1   0                                                               5-10                                                  __________________________________________________________________________

EXAMPLE 7

An intermediate layer, 0.1 μ thick, of diallyl phthalate resin (DISODAPB supplied by Osaka Soda Co.) was formed on the outer surface of analuminum drum having a diameter of 60 mm. On this intermediate layer wasformed a carrier generating layer, 0.5 μ in dry thickness, by coating onthe intermediate layer a dispersion prepared by adding 2 g of theaforementioned azo pigment No. I-23 to a solution containing 2 g ofpolyarylate resin dissolved in 100 ml of tetrahydrofuran and dispersingin a paint conditioner for about 3 hours and drying the coating. On thiscarrier generating layer was formed a carrier transfer layer, 15 μ indry thickness, by coating a solution prepared by dissolving 10 g of acarrier transfer material,N,N-diethylaminobenzaldehyde-1-(phenyl)-1-methylhydrazone represented bythe following formula: ##STR304## and 12 g of polycarbonate resin(PANLITE L supplied by Teijin Limited) in 100 ml of 1,2-dichloroethaneand then drying the coating to obtain the photoreceptor of thisinvention.

This electrophotographic photoreceptor was mounted on a commercialelectrophotographic copier of the cartridge type, which had beenpartially modified and reproduction was carried out to obtain a clearimage high in contrast and faithful to original.

Reproduction was repeated 1000 times and there were obtained visibleimages which remained throughout the same in quality as the first copy.

EXAMPLE 8

The drum-type electrophotographic photoreceptor obtained in Example 7was examined for reflection spectrum by an integrating spherespectrophotometer (UV-365 of Shimadzu Seisakusho Ltd.). As a result, itwas found that the absorption maxima in the visible region were ataround 650-690 nm.

It was recognized that the photoreceptor of this invention can endurethe actual use under exposure to a light source such as light-emittingdiode and He-Ne laser beam.

EXAMPLE 9

A styrene-n-butyl methacrylate-methacrylic acid copolymer(styrene:n-butyl methacrylate=1:2 (weight ratio) and acid value: 250),the aforementioned azo pigment No. I-35 and2-phenyl-1-ethylindole-3-aldehyde 1,1-diphenylhydrazone were mixed at aweight ratio of 1.5 : 0.2 : 1.1. A coating composition was prepared fromsaid mixture and dioxane (the resin component and the hydrazone compoundwere dissolved while the azo pigment was dispersed in the dioxane) andthis coating composition was coated on a surface of oxidized and grainedAl plate and dried to produce a single-layer type photoreceptor of 6 μin film thickness. The resulting photoreceptor was tested for theelectrophotographic characteristics by the above used electrostaticpaper testing apparatus to obtain the following results.

Applied potential: +6 KV

V_(o) =520 volt

E_(1/2=) 4.1 lux·sec.

The photoreceptor was subjected to development treatment with adeveloper (toner) to form a visible image, then treated with an alkalineprocessing aqueous solution (e.g. a solution containing 3% oftriethanolamine, 10% of ammonium carbonate, 15% of polyethylene glycolhaving an average molecular weight of 190-210 and 5% of benzyl alcohol)to dissolve the photosensitive layer in non-image areas and washed withwater containing sodium silicate to obtain a printing plate.

Offset printing was carried out using this printing plate to find thatthis printing plate was able to stand printing of about 100,000 copies.

The optimum amount of exposure to obtain the visible toner images was150 lux·sec (light source: halogen lamp). The printing plate wasdirectly made without using a block copy.

EXAMPLES 10-11

On an aluminum plate was formed an intermediate layer, 0.1 μ thick, ofdiallyl phthalate resin (DAISODAP B supplied by Osaka Soda Co.) and acarrier generating layer, 0.5 μ in dry thickness, was formed thereon bycoating on the intermediate layer a dispersion prepared by adding 2 g ofan azo pigment to a solution comprising 2 g of polyarylene resindissolved in 100 ml of tetrahydrofuran and dispersing in a paintconditioner for about 3 hours and drying the coating. A carrier transferlayer, 15 μ in dry thickness, was formed thereon by coating on thecarrier generating layer a solution comprising 10 g of a carriertransfer material represented by the following formula: ##STR305## and12 g of polyacrylate resin dissolved in 100 ml of 1,2-dichloroethane anddrying the coating to obtain a drum-type electrophotographicphotoreceptor.

Two photoreceptors were produced using the aforementioned pigment Nos.I-105 and I-112 as the azo pigments.

These photoreceptors were left to stand in the dark place at 30° C. forone day and thereafter was mounted on an electrostatic paper testingapparatus (SP-428 of Kawaguchi Denki Seisakusho Co.) and tested forcharacteristics in the following manner.

That is, the photosensitive layer was electrostatically charged bysubjecting it for 5 seconds to corona discharge produced by applying apotential of -6 KV from a charger and the surface potential V_(o) (-V)at that time and a surface potential Vd (-V) after lapse of 10 secondswere measured and DD=Vd/V_(o) ×100(%) was obtained. The charged surfacewas exposed to a halogen lamp, the illuminance on the surface being 30lux, and the exposure E_(1/2) (lux·sec) required for decaying thesurface potential to 1/2 was obtained. Then, this photoreceptor wasexposed to fluorescent lamp of 5000 lux for 5 minutes and, after left tostand in the dark place for 30 seconds, was tested for thecharacteristics in the same manner as above to obtain V_(o) (-V),E_(1/2) (lux·sec) and DD (%). The results are shown in Table 3.

The initial characteristics are shown in the upper column and thecharacteristics after exposure to light are shown in the lower column inTable 3.

                  TABLE 3                                                         ______________________________________                                        Azo pigment    V.sub.o (-V)                                                                           E.sub.2/1 (lux · sec)                                                            DD (%)                                    ______________________________________                                        Example 10                                                                            I-105      1010     1.7       92                                                          820     1.2       84                                      Example 11                                                                            I-112      1030     1.7       93                                                          840     1.1       82                                      ______________________________________                                    

The results of Table 3 show that photoreceptors containing the azopigment Nos. I-105 and I-112 of this invention are markedly superior inall of surface potential V_(o), sensitivity and preexposurecharacteristic.

Then, after having received an exposure of 50 lux·second, thephotoreceptors were tested for the surface potential, namely, residualpotnetial E₅₀ (-V). Similar test cycle was repeated 500 times. In eachcycle, complete removal of the residual potential was performed byexposing to a tungsten lamp for 0.3 second at an illuminance of 300 lux.The results obtained are shown in Table 4. The results show thatphotoreceptors containing the azo pigment Nos. I-105 and I-112 are alsosuperior in characteristics of repeated use.

                                      TABLE 4                                     __________________________________________________________________________                 First cycle   500th cycle                                                     V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                                                          V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                 Azo pigment  (-V)                                                                              (lux · sec)                                                                (-V)                                                                              (-V)                                                                              (lux · sec)                                                                (-V)                                     __________________________________________________________________________    Example 10                                                                          I-105  1010                                                                              1.7   0-5 1000                                                                              1.8   0-5                                      Example 11                                                                          I-112  1030                                                                              1.7   0-5 1010                                                                              1.7   0-5                                      __________________________________________________________________________

EXAMPLES 12-17

An aluminum drum of 60 mm in diameter was provided on the exteriorsurface with an intermediate layer, 0.05 μ in thickness, comprising avinyl chloride-maleic anhydride copolymer (ESUREK MF-10 of SekisuiChemical Co.). A carrier generating layer, 0.3 μ in dry thickness, wasformed by coating said intermediate layer with an azo pigment dispersionprepared by adding 2 g of an azo pigment and 1 g of butyral resin(ESUREK B of Sekisui Chemical Co.) to 100 ml of tetrahydrofuran anddispersing in a paint conditioner for about 1 hour, and drying thecoating. A carrier transfer layer, 19 μ in dry thickness, was formed byovercoating said carrier generating layer with a solution prepared bydissolving 5 g of N,N-dibenzylaminobenzaldehyde-1,1-diphenylhydrazone, acarrier transfer material and 7 g of polyarylate resin in 50 ml of1,2-dichloroethane and drying the coating. Thus, electrophotographicphotoreceptor was obtained.

In this way, 6 electrophotographic photoreceptors were prepared by usingthe aforementioned pigment Nos. I-107, I-109, I-113, I-115, I-119 andI-120.

These photoreceptors were mounted on a commercial electrophotographiccopier of cartridge type which had been partially modified by us andreproduction of an original including red images was carried out toobtain a copy which was good in reproducibility of the red images.

The photoreceptors were tested for pre-exposure characteristics andrepeated copying ability of 1000 times to find that the photoreceptorsof this invention were superior in these characteristics.

EXAMPLE 18

Example 1 was repeated except that pigment No. I-77 was used in place ofI-12. The results are shown in Table 5.

                  TABLE 5                                                         ______________________________________                                                      1st cycle                                                                            500th cycle                                              ______________________________________                                        V.sub.o (-V)    970      940                                                  E.sub.1/2  (lux · second)                                                            1.8      1.7                                                  E.sub.50 (-V)   0-5      about 10                                             ______________________________________                                    

EXAMPLES 19-23

Five electrophotographic photoreceptors of this invention were preparedin the same manner as in Example 1 except that the aforementioned azopigment Nos. I-66, I-78, I-83, I-84 and II-95 were used as carriergenerating materials. They were tested for characteristics in the samemanner as in Example 1. The results are shown in Table 6.

                                      TABLE 6                                     __________________________________________________________________________                  First cycle   500th cycle                                                     V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                                                          V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                Example                                                                            Azo pigments                                                                           (-V)                                                                              (lux · sec)                                                                (-V)                                                                              (-V)                                                                              (lux · sec)                                                                (-V)                                    __________________________________________________________________________    19   Pigment No. I-66                                                                        960                                                                              2.5   about                                                                              950                                                                              2.4   about                                                           15            20                                      20   Pigment No. I-78                                                                       1020                                                                              1.9   0-5 1010                                                                              1.9   0-5                                     21   Pigment No. I-83                                                                       1000                                                                              1.8   0-5 1000                                                                              1.8   0-5                                     22   Pigment No. I-84                                                                        980                                                                              2.1    5-10                                                                              980                                                                              2.0   about                                                                         10                                      23   Pigment No. II-95                                                                       970                                                                              2.8   about                                                                              940                                                                              2.7   about                                                           20            30                                      __________________________________________________________________________

EXAMPLE 24

Example 1 was repeated except that No. II-4 was used as an azo pigment.The results are shown in Table 7.

                  TABLE 7                                                         ______________________________________                                                      1st cycle                                                                            500th cycle                                              ______________________________________                                        V.sub.o (-V)    780      760                                                  E.sub.1/2  (lux · second)                                                            1.8      1.7                                                  E.sub.50 (-V)   about 5  0                                                    ______________________________________                                    

EXAMPLES 25-29

Five electrophotographic photoreceptors of this invention were preparedin the same manner as in Example 24 except that the azo pigment Nos.II-2, II-6, II-15, II-18 and II-51 were used as carrier generatingmaterials and these were tested for characteristics in the same manner.The results are shown in Table 8.

                                      TABLE 8                                     __________________________________________________________________________                  First cycle   500th cycle                                                     V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                                                          V.sub.o                                                                           E.sub.1/2                                                                           E.sub.50                                Example                                                                            Azo pigment                                                                            (-V)                                                                              (lux · sec)                                                                (-V)                                                                              (-V)                                                                              (lux · sec)                                                                (-V)                                    __________________________________________________________________________    25   Pigment No. II-2                                                                        960                                                                              2.8   about                                                                              940                                                                              2.7   0                                                               10                                                    26   Pigment No. II-6                                                                       1080                                                                              2.7   about                                                                             1040                                                                              2.6   0                                                               10                                                    27   Pigment No. II-15                                                                      1040                                                                              1.9   about                                                                             1000                                                                              1.9   0                                                               0-5                                                   28   Pigment No. II-18                                                                      1010                                                                              2.1   about                                                                              990                                                                              2.0   0                                                               5                                                     29   Pigment No. II-51                                                                       980                                                                              1.9   about                                                                              940                                                                              1.9   0                                                               0-5                                                   __________________________________________________________________________

EXAMPLE 30

An aluminum drum of 60 mm in diameter was provided on the exteriorsurface with an intermediate layer, 0.1 μ in thickness, comprising abutyral resin (polymerization degree about 700, Wako Junyaku Co.). Acarrier generating layer, 0.5 μ in dry thickness, was formed by coatingsaid intermediate layer with a dispersion prepared by adding 2 g of theaforementioned azo pigment No. II-10 to 100 ml of tetrahydrofurancontaining 2 g of polyarylate resin dissolved therein and dispersing ina paint conditioner for about 3 hours, and drying the coating. A carriertransfer layer, 15 μ in dry thickness, was formed by overcoating saidcarrier generating layer with a solution prepared by dissolving 10 g ofN,N-diethylaminobenzaldehyde-1-(4'-methoxyphenyl)-1-allylhydrazone, acarrier transfer material of the structural formula: ##STR306## and 12 gof polycarbonate resin (Panlite L-1250 of Teijin Ltd.) in 100 ml of1,2-dichloroethane and drying the coating. Thus drum-typeelectrophotographic photoreceptor was obtained.

This photoreceptor was mounted on a commercial electrophotographiccopier of cartridge type which had been partially modified by us andreproduction was carried out to obtain an visible image high in contrastand faithful to original.

Reproduction was repeated 1000 times to obtain visible image remainedthroughout the same in quality.

EXAMPLE 31

The drum-type photoreceptor obtained in Example 30 was examined forreflection spectrum by means of an integrating sphere spectrophotometerUV-365 of Shimadzu Seisakusho Ltd.) to find that absorption maxima ofthis photoreceptor in visible region was at 640 nm and 670 nm. Thespectral sensitivities at 640 nm and 670 nm were measured as energyrequired for decay from -600 V to -100 V to obtain 5.4 erg/cm² and 5.8erg/cm², respectively. This indicates that the photoreceptor is able toendure actual use under exposure to a light source such aslight-emitting diode or He-Ne laser beam.

What is claimed is:
 1. An electrophotographic photoreceptor whichcomprises an electroconductive support and, provided thereon, aphotosensitive layer containing an azo pigment represented by thefollowing formula (I): ##STR307## wherein A is selected from the groupconsisting of a hydrogen atom, an alkyl group, a phenyl group or aheterocyclic ring group, n is 0 or 1 and Cp is a coupler residue.
 2. Anelectrophotographic photoreceptor according to claim 1 wherein thephotosensitive layer comprises a dispersion of the azo pigment in abinder.
 3. An electrophotographic photoreceptor according to claim 1wherein the photosensitive layer comprises a charge generating layercontaining the azo pigment as a charge generating material and a chargetransfer layer containing a charge transfer material.
 4. Anelectrophotographic photoreceptor according to claim 1, wherein the azopigment represented by the formula (I) is a pigment represented by theformula: ##STR308## wherein A is selected from the group consisting of ahydrogen atom, an alkyl group, a phenyl group or a heterocyclic ringgroup, n is 0 or 1 and Cp is a coupler residue.
 5. Anelectrophotographic photoreceptor which comprises an electroconductivesupport and, provided thereon, a photosensitive layer containing an azopigment represented by the formula: ##STR309## wherein A is selectedfrom the group consisting of a hydrogen atom, an alkyl group, a phenylgroup, or a heterocyclic ring group and Cp is a coupling residue.
 6. Anelectrophotographic photoreceptor which comprises an electroconductivesupport and, provided thereon, a photosensitive layer containing an azopigment represented by the formula: ##STR310## wherein R1 is selectedfrom the group consisting of a hydrogen atom; a lower alkyl group, alower alkoxy group, or a halogen atom and Cp is a coupler residuerepresented by the formula: ##STR311## wherein R2 is selected from thegroup consisting of a hydrogen atom, a lower alkyl group, a lower alkoxygroup, or a halogen atom.
 7. An electrophotographic photoreceptor whichcomprises an electroconductive support and, provided thereon, aphotosensitive layer containing an azo pigment represented by thefollowing formula (II): ##STR312## wherein R₁ is selected from the groupconsisting of a hydrogen atom, a lower alkyl group, a lower alkoxy groupor a halogen atom, Cp is represented by the following formula:##STR313## wherein R₂ is selected from the group consisting of ahydrogen atom, a lower alkyl group, a lower alkoxy group or a halogenatom, n is 0 or 1, l and p each is 1 or 2 and when l and p are 2, thetwo R₁ and the two R₂ may be identical or different, respectively.
 8. Anelectrophotographic photoreceptor according to claim 7, wherein the azopigment represented by the formula (II) is a pigment represented by theformula: ##STR314## wherein R₁ is selected from the group consisting ofa hydrogen atom, a lower alkyl group, a lower alkoxy group or a halogenatom, Cp is represented by the following formula: ##STR315## wherein R₂is selected from the group consisting of a hydrogen atom, a lower alkylgroup, a lower alkoxy group or a halogen atom, n is 0 or 1, l and p eachis 1 or 2 and when l and p are 2, the two R₁ and the two R₂ may beidentical or different, respectively.
 9. An electrophotographicphotoreceptor according to claim 7 wherein the photosensitive layercomprises a dispersion of the azo pigment in a binder.
 10. Anelectrophotographic photoreceptor according to claim 7, wherein thephotosensitive layer contains the azo pigment and a charge transfermaterial.
 11. An electrophotographic photoreceptor according to claim 7wherein the photosensitive layer comprises a charge generating layercontaining the azo pigment as a charge generating material and a chargetransfer layer containing a charge transfer material.